W-rich mixed oxide solid solutions under pressure

M. Yu Petrushina, E. S. Dedova, K. V. Yusenko, A. S. Portnyagin, E. K. Papynov, E. Yu Filatov, S. V. Korenev, A. I. Gubanov

Результат исследования: Научные публикации в периодических изданияхстатья по материалам конференции

Аннотация

We report high-pressure synchrotron X-ray powder diffraction data for the W-rich cubic ZrW2-xMoxO8 (x=0.4) up to 10 GPa with open decompression. This study shows that cubic-ZrW1.6Mo0.4O8 transforms to orthorhombic phase at the 5.04 GPa. Pressure-induced reversable amorphization of material was observed at 8.13 GPa. The obtained data suggest that W-rich cubic ZrW2-xMoxO8 (x=0.4) solid solutions are more attractive for creating products working under extreme conditions and mechanic stress.

Язык оригиналаанглийский
Номер статьи012037
ЖурналJournal of Physics: Conference Series
Том1611
Номер выпуска1
DOI
СостояниеОпубликовано - 25 авг 2020
Событие17th International Conference of Students and Young Scientists on Prospects of Fundamental Sciences Development, PFSD 2020 - Tomsk, Российская Федерация
Продолжительность: 21 апр 202024 апр 2020

Fingerprint Подробные сведения о темах исследования «W-rich mixed oxide solid solutions under pressure». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать