Thermolysis of ferric oxalate in structured mesoporous silica

P. Yu. Tyapkin, S. A. Petrov, A. P. Chernyshev, K. B. Gerasimov, N. F. Uvarov

Результат исследования: Научные публикации в периодических изданияхстатья по материалам конференциирецензирование

1 Цитирования (Scopus)


The influence of mesoporous silica matrix on the thermolysis of ferric oxalate loaded into its pores was studied. A significant decrease in the onset of the thermal decomposition temperature of ferric oxalate was observed. The maximum of the second decomposition stage of ferric oxalate in argon atmosphere was also appeared to be shifted by 30-40°C when thermolysis occurred in pores. These effects were accounted for the amorphous state of ferric oxalate and enhanced reactivity of highly dispersed particles.

Язык оригиналаанглийский
Страницы (с-по)17-20
Число страниц4
ЖурналMaterials Today: Proceedings
СостояниеОпубликовано - 1 янв. 2019
Событие5th International Conference on Fundamental Bases of Mechanochemical Technologies (FBMT) - Novosibirsk
Продолжительность: 25 июн. 201828 июн. 2018


Подробные сведения о темах исследования «Thermolysis of ferric oxalate in structured mesoporous silica». Вместе они формируют уникальный семантический отпечаток (fingerprint).