Thermodynamic Study of Lithium Tungstate Single Crystals Doped by Molybdenum (Li2W1- xMo xO4, x = 0.1 and 0.15)

Nata I. Matskevich, Vladimir N. Shlegel, Anna N. Semerikova, Mariya Yu Matskevich

Результат исследования: Научные публикации в периодических изданияхстатья

1 Цитирования (Scopus)

Аннотация

The single crystals Li2W0.85Mo0.15O4 and Li2W0.9Mo0.1O4 have been grown by a low-temperature-gradient Czochralski technique as representatives of promising materials for scintillating cryogenic bolometers. Thermodynamic properties and their relationship with structural parameters to improve and extend the device portfolio with special emphasis on formation enthalpies, thermodynamic stability, and lattice enthalpies have been revealed. Solution enthalpies of Li2CO3, MoO3, and Li2W0.85Mo0.15O4 and Li2W0.9Mo0.1O4 single crystals have been measured in 0.40162 mol kg-1 aqueous KOH. The standard formation enthalpies (ΔfH0 (Li2W0.85Mo0.15O4, s, 298.15 K) = -1590.8 ± 2.0 kJ mol-1 ΔfH0 (Li2W0.9Mo0.1O4, s, 298.15 K) = -1594.1 ± 2.3 kJ mol-1), formation enthalpies from simple oxides, and lattice enthalpies have been determined. As a result, the dependences of formation enthalpies and lattice enthalpies for Li2W1-xMoxO4 on tolerance factors have been found to be linear. It has been discovered that the thermodynamic stability and lattice enthalpies of Li2W1-xMoxO4 are increased when the tolerance factor tends to one. It has been established that single crystals Li2W0.85Mo0.15O4 and Li2W0.9Mo0.1O4 are several times more thermodynamically stable than ZnMoO4 and CdWO4

Язык оригиналаанглийский
Страницы (с-по)1523-1530
Число страниц8
ЖурналJournal of Chemical and Engineering Data
Том65
Номер выпуска4
DOI
СостояниеОпубликовано - 9 апр 2020

Fingerprint Подробные сведения о темах исследования «Thermodynamic Study of Lithium Tungstate Single Crystals Doped by Molybdenum (Li<sub>2</sub>W<sub>1- x</sub>Mo <sub>x</sub>O<sub>4</sub>, x = 0.1 and 0.15)». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать