The Concentration Quenching of Photoluminescence and the Quantum Yield in (Y1–xPrx)2O2Se Solid Solutions

M. S. Tarasenko, A. A. Ryadun, Zh K. Orazov, T. A. Pomelova, V. B. Zalesskii, V. V. Malyutina-Bronskaya, V. E. Fedorov, H. Ch Wang, N. G. Naumov

Результат исследования: Научные публикации в периодических изданияхстатьярецензирование

Аннотация

(Y1–xPrx)2O2Se solid solutions with х = 0.004, 0.008, 0.010, 0.012, and 0.020 have been prepared from oxides by ampule synthesis. We have measured their excitation spectra at λem = 514 nm and their photoluminescence and quantum yield spectra at λex = 463 nm (T = 300 K). Comparing their emission intensities at wavelengths of 514 (3P03H4 transition) and 670 nm (3P03F2 transition), we have determined the optimal dopant concentration (x = 0.01), at which the quantum yield has a maximum, reaching 3%.

Язык оригиналаанглийский
Страницы (с-по)830-834
Число страниц5
ЖурналInorganic Materials
Том57
Номер выпуска8
DOI
СостояниеОпубликовано - авг 2021

Предметные области OECD FOS+WOS

  • 2.05 ТЕХНОЛОГИЯ МАТЕРИАЛОВ
  • 2.04 ХИМИЧЕСКИЕ ТЕХНОЛОГИИ
  • 1.04 ХИМИЧЕСКИЕ НАУКИ

Fingerprint

Подробные сведения о темах исследования «The Concentration Quenching of Photoluminescence and the Quantum Yield in (Y<sub>1–x</sub>Pr<sub>x</sub>)<sub>2</sub>O<sub>2</sub>Se Solid Solutions». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать