Technological characteristics of epoxy/carbon black composites

A. G. Bannov, A. E. Brester, A. A. Shestakov, M. V. Popov, N. I. Lapekin, G. K. Krivyakin

Результат исследования: Научные публикации в периодических изданияхстатья по материалам конференциирецензирование

1 Цитирования (Scopus)

Аннотация

The set of epoxy composites based on Alfa AesarTM carbon black (CB) (0-1.5 wt%) has been prepared. Dependence of shaft torque on the rotation frequency in batch mixer with overhead stirrer for epoxy/ CB system was obtained. Chemical resistance tests of epoxy resin/carbon black composites were carried out by sample immersion in 30% H2SO4 and 95% H2SO4. The increase of apparent viscosity of epoxy/CB mixture was observed for relatively low temperatures (30-40 °C). Immersion of epoxy/CB composite in concentrated H2SO4 induced strong oxidation of sample and mass loss. Dilution of sulfuric acid led to the mass gain of the composite sample due to the increased uptake. The improvement of chemical resistance of epoxy/CB composites was observed in 95% H2SO4

Язык оригиналаанглийский
Страницы (с-по)496-498
Число страниц3
ЖурналMaterials Today: Proceedings
Том31
DOI
СостояниеОпубликовано - 2020
Событие6th International Russian-Kazakhstan Conference on Chemical Technologies of Functional Materials, RKFM 2020 - Almaty, Казахстан
Продолжительность: 9 апр 202010 апр 2020

Fingerprint

Подробные сведения о темах исследования «Technological characteristics of epoxy/carbon black composites». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать