Pt-Fe nanoalloy: Structure evolution study and catalytic properties in water gas shift reaction

Anna Gorlova, Andrey Zadesenets, Evgeniy Filatov, Pavel Simonov, Sergey Korenev, Olga Stonkus, Vladimir Sobyanin, Pavel Snytnikov, Dmitriy Potemkin

Результат исследования: Научные публикации в периодических изданияхстатьярецензирование

Аннотация

In the present work we studied the properties of Pt0.5Cu0.5, Pt0.5Fe0.5, Pt0.33Ag0.67, Pt0.6Au0.4 nanoalloys in water gas shift (WGS) reaction for the first time. Cu, Fe, Ag, Au were chosen as modifiers due to the low catalytic activity in undesirable side reactions of carbon oxides methanation. Nanoalloys were synthesized via corresponding double complex salts decomposition, which provided the selective formation of bimetallic nanoparticles. A simulated reformate gas mixture, containing (vol.%) 10 CO, 15 CO2, 30 H2O and 45 H2, was used to evaluate the activity of these systems. Only Pt0.5Fe0.5 nanopowder was active, while Pt-FeOx metal-oxide composite was inert. The positive effect of Pt-Fe alloying on WGS performance was also confirmed for silica supported catalysts. TG and XRD in situ analysis reveal that Pt0.5Fe0.5 is stable toward oxidation under WGS reaction conditions (T < 350°C, reductive atmosphere), while Pt-FeOx undergoes partial reduction but without formation of Pt-Fe alloy nanoparticles.

Язык оригиналаанглийский
Номер статьи111727
ЖурналMaterials Research Bulletin
Том149
DOI
СостояниеОпубликовано - мая 2022

Предметные области OECD FOS+WOS

  • 2.05 ТЕХНОЛОГИЯ МАТЕРИАЛОВ
  • 2.03 МЕХАНИКА И МАШИНОСТРОЕНИЕ
  • 1.03.UK ФИЗИКА КОНДЕНСИРОВАННОГО СОСТОЯНИЯ

Fingerprint

Подробные сведения о темах исследования «Pt-Fe nanoalloy: Structure evolution study and catalytic properties in water gas shift reaction». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать