Pressure induced change in the ZrWMoO8

M. Yu Petrushina, E. S. Dedova, K. V. Yusenko, A. S. Portnyagin, E. K. Papynov, E. Yu Filatov, A. I. Gubanov

Результат исследования: Научные публикации в периодических изданияхстатья по материалам конференции

1 Цитирования (Scopus)

Аннотация

In this paper we report high-pressure synchrotron x-ray powder diffraction data for the cubic ZrWMoO8. For the first time, extensive structural study of ZrWMoO8 solid solution as a function of pressure was performed. This study shows that disordered cubic-ZrWMoO8 (space group Pa3-) transforms to ordered cubic-ZrWMoO8 (space group P213) at low pressure. A further high-pressure influence leads followed by amorphization of the sample at 2.2 GPa. All transformations are irreversible. Our work will have high impact in the design of new composite materials with well-defined thermal expansion, especially for applications under extreme conditions and high mechanic stress.

Язык оригиналаанглийский
Страницы (с-по)428-430
Число страниц3
ЖурналMaterials Today: Proceedings
Том25
DOI
СостояниеОпубликовано - 1 окт 2019
Событие3rd All-Russian Conference, with International Participation Hot Topics of Solid State Chemistry : From New Ideas to New Materials, HTSSC 2019 - Novosibirsk, Российская Федерация
Продолжительность: 1 окт 20195 окт 2019

Fingerprint Подробные сведения о темах исследования «Pressure induced change in the ZrWMoO<sub>8</sub>». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать