[NiEn3](MoO4)0.5(WO4)0.5 co-crystals as single-source precursors for ternary refractory ni–mo–w alloys

Результат исследования: Научные публикации в периодических изданияхстатьярецензирование

Аннотация

The co-crystallisation of [NiEn3 ](NO3)2 (En = ethylenediamine) with Na2MoO4 and Na2WO4 from a water solution results in the formation of [NiEn3 ](MoO4)0.5 (WO4)0.5 co-crystals. According to the X-ray diffraction analysis of eight single crystals, the parameters of the hexagonal unit cell (space group P–31c, Z = 2) vary in the following intervals: a = 9.2332(3)–9.2566(6); c = 9.9512(12)–9.9753(7) Å with the Mo/W ratio changing from 0.513(3)/0.487(3) to 0.078(4)/0.895(9). The thermal decomposition of [NiEn3 ](MoO4)0.5 (WO4)0.5 individual crystals obtained by co-crystallisation was performed in He and H2 atmospheres. The ex situ X-ray study of thermal decomposition products shows the formation of nanocrystalline refractory alloys and carbide composites containing ternary Ni–Mo–W phases. The formation of carbon–nitride phases at certain stages of heating up to 1000C were shown.

Язык оригиналаанглийский
Номер статьи3272
ЖурналNanomaterials
Том11
Номер выпуска12
DOI
СостояниеОпубликовано - дек. 2021

Предметные области OECD FOS+WOS

  • 2.04 ХИМИЧЕСКИЕ ТЕХНОЛОГИИ
  • 2.05 ТЕХНОЛОГИЯ МАТЕРИАЛОВ

Fingerprint

Подробные сведения о темах исследования «[NiEn3](MoO4)0.5(WO4)0.5 co-crystals as single-source precursors for ternary refractory ni–mo–w alloys». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать