Influence of post-deposition annealing under magnetic field on the structure of phthalocyanine thin films

Tamara V. Basova, Irina V. Jushina, Asim K. Ray

Результат исследования: Научные публикации в периодических изданияхстатья

4 Цитирования (Scopus)

Аннотация

A comparative analysis of the influence of post deposition annealing process without and under applied magnetic field of 1 T, on structure and morphology of VOPcF16 films, has been carried out. The phase transition of VOPcF16 film upon its annealing under applied magnetic film was studied by the methods of UV–Visible and Raman spectroscopies as well as atomic force microscopy. It was shown that the temperature of the phase transition of VOPcF16 decreases from 160 to 100 °C, when magnetic field is applied during post deposition annealing. The formation of VOPcF16 films with elongated crystallites oriented preferably in one direction was observed after their annealing in magnetic field. The current–voltage characteristic measurements demonstrated an increase in the lateral conductivity for the films annealed under applied magnetic field in comparison with the films annealed without magnetic field.

Язык оригиналаанглийский
Страницы (с-по)4716-4721
Число страниц6
ЖурналJournal of Materials Science: Materials in Electronics
Том26
Номер выпуска7
DOI
СостояниеОпубликовано - 24 июл 2015

Fingerprint Подробные сведения о темах исследования «Influence of post-deposition annealing under magnetic field on the structure of phthalocyanine thin films». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать