Consolidation of Nanocrystals of Detonation Nanodia-mond under Thermobaric Sintering

D. G. Bogdanov, V. A. Plotnikov, A. S. Bogdanov, S. V. Makarov, V. G. Vins, Александр Павлович Елисеев, Aleksei Chepurov

Результат исследования: Научные публикации в периодических изданияхстатья

Аннотация

The structural and physicomechanical properties of composite materials obtained by sintering detonation nanodiamonds under high pressures and temperatures (P = 5 GPa, T = 1200°C) have been investigated. There is a slight growth of diamond crystals after sintering from 4.5 to 5.2 nm. It is shown that the strength of the samples locally reaches 14 GPa. The high microhardness of the material is due to the consolidation of diamond nanocrystals into strong polycrystalline aggregates owing to the formation of covalent bonds between crystals under high pressure and temperature conditions.

Язык оригиналаанглийский
Страницы (с-по)103–108
Число страниц6
ЖурналInorganic Materials
Том10
Номер выпуска1
DOI
СостояниеОпубликовано - 1 янв 2019
Опубликовано для внешнего пользованияДа

Fingerprint Подробные сведения о темах исследования «Consolidation of Nanocrystals of Detonation Nanodia-mond under Thermobaric Sintering». Вместе они формируют уникальный семантический отпечаток (fingerprint).

  • Цитировать

    Bogdanov, D. G., Plotnikov, V. A., Bogdanov, A. S., Makarov, S. V., Vins, V. G., Елисеев, А. П., & Chepurov, A. (2019). Consolidation of Nanocrystals of Detonation Nanodia-mond under Thermobaric Sintering. Inorganic Materials, 10(1), 103–108. https://doi.org/10.1134/S2075113319010040