The phase transformations of stoichiometric HfO2 and non-stoichiometric HfOx oxides grown by ion-beam sputtering-deposition during their electron beam crystallization were investigated. It was found that the sequences of crystalline phase formations in stoichiometric and non-stoichiometric oxides are significantly different. An amorphous HfO2 film crystallizes first to form monoclinic α-HfO2 phase nanocrystals and then tetragonal β-HfO2 phase nanocrystals. In non-stoichiometric HfOx oxides (x = 1.82), in contrast to HfO2 oxides, hexagonal α-Hf phase metal clusters were initially present. During the crystallization process, the metallic α-Hf phase growth was observed first with the simultaneous appearance of the monoclinic α-HfO2 phase. Then the orthorhombic-I γ-HfO2 phase appeared, while the α-Hf phase growth ceased. The composition of the investigated non-stoichiometric HfOx oxides was chosen to be the same as in the dielectric layer of resistive memory cells (ReRAM). The crystallization of oxides was carried out in a local region, the sizes of which are comparable with the size of the ReRAM filament. This made it possible to partially project the crystallization results onto the forming and switching processes in ReRAM cells.
Предметные области OECD FOS+WOS
- 2.07 ЭНЕРГЕТИКА И РАЦИОНАЛЬНОЕ ПРИРОДОПОЛЬЗОВАНИЕ
- 1.02 КОМПЬЮТЕРНЫЕ И ИНФОРМАЦИОННЫЕ НАУКИ
- 1.03 ФИЗИЧЕСКИЕ НАУКИ И АСТРОНОМИЯ
- 2.02 ЭЛЕКТРОТЕХНИКА, ЭЛЕКТРОННАЯ ТЕХНИКА, ИНФОРМАЦИОННЫЕ ТЕХНОЛОГИИ
- 1.05 НАУКИ О ЗЕМЛЕ И СМЕЖНЫЕ ЭКОЛОГИЧЕСКИЕ НАУКИ
- 1.06 БИОЛОГИЧЕСКИЕ НАУКИ