Aluminum Matrix Composites Reinforced with Cu9Al4 Particles: Mechanochemical Synthesis and Consolidation by the Spark Plasma Sintering

T. F. Grigoreva, D. V. Dudina, S. A. Petrova, S. A. Kovaleva, I. S. Batraev, S. V. Vosmerikov, E. T. Devyatkina, N. Z. Lyakhov

    Результат исследования: Научные публикации в периодических изданияхстатьярецензирование

    Аннотация

    X-ray analysis and scanning electron microscopy have been used to study mechanochemically synthesized Al/10 wt % Cu9Al4 and Al/20 wt % Cu9Al4 composites and sintered materials based on them. As a modifiers, powders of the mechanosynthesized nanostructured Cu9Al4 intermetallic compound were used. It has been shown that the composite structure with the uniform distribution of the Cu9Al4 particles in the aluminum matrix is formed during mechanical activation even for 1 min. In the course of mechanical activation of the powder mixtures of Al with 10 and 20 wt % Cu9Al4 the size of intermetallic crystallites grows by 2.3–3 times to 7 and 9 nm, respectively. After spark plasma sintering of the Al/Сu9Al4 composites, the uniform distribution of reinforcing particles retains for their content up to 20 wt %. The hardness of sintered composites is 60–77 HV, which is ~2 times higher than the hardness of aluminum without additives of the strengthening phase.

    Язык оригиналаанглийский
    Страницы (с-по)768-774
    Число страниц7
    ЖурналPhysics of Metals and Metallography
    Том122
    Номер выпуска8
    DOI
    СостояниеОпубликовано - авг 2021

    Предметные области OECD FOS+WOS

    • 2.05.PZ МЕТАЛЛУРГИЯ И МЕТАЛЛУРГИЧЕСКАЯ ИНЖЕНЕРИЯ

    Fingerprint

    Подробные сведения о темах исследования «Aluminum Matrix Composites Reinforced with Cu<sub>9</sub>Al<sub>4</sub> Particles: Mechanochemical Synthesis and Consolidation by the Spark Plasma Sintering». Вместе они формируют уникальный семантический отпечаток (fingerprint).

    Цитировать