Al2O3/InGaAs interface passivation by fluorine-containing anodic layers

M. S. Aksenov, N. A. Valisheva, D. V. Gorshkov, G. Y. Sidorov, I. P. Prosvirin, A. K. Gutakovskii

Результат исследования: Научные публикации в периодических изданияхстатьярецензирование

Аннотация

The morphology, chemical composition, and electronic properties of Al2O3/InGaAs interfaces with and without anodic oxide layers, formed in DC plasma (O2, Ar) with different contents of the fluorinating component (CF4), were studied. It is shown that thin fluorinated anodic oxide layers, in combination with annealing at 300 °C, reduce the density of interface states by a factor of 3-4 over the entire bandgap. The minimum state density values near the midgap determined by the Terman method are about 2 × 1012 eV-1 cm-2. However, it is demonstrated that, in contrast to the Al2O3/InGaAs interface, the interface with a fluorinated oxide is not stable and degrades when heated above 300 °C.

Язык оригиналаанглийский
Номер статьи085301
ЖурналJournal of Applied Physics
Том131
Номер выпуска8
DOI
СостояниеОпубликовано - 28 февр. 2022

Предметные области OECD FOS+WOS

  • 1.03 ФИЗИЧЕСКИЕ НАУКИ И АСТРОНОМИЯ

Fingerprint

Подробные сведения о темах исследования «Al2O3/InGaAs interface passivation by fluorine-containing anodic layers». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать