2D printed graphene conductive layers with high carrier mobility

Evgenyi Yakimchuk, Regina Soots, Igor Kotin, Irina Antonova

Результат исследования: Научные публикации в периодических изданияхстатьярецензирование

12 Цитирования (Scopus)

Аннотация

The comparison of different suspensions, obtained from the same material source subjected to electrochemical exfoliation and to analogous auxiliary treatments, but in different solutions, allowed choosing the most effective approach to obtaining graphene suspensions. It was found for the layers with a thickness of 10–20 nm printed from a water-based suspension that the sheet resistance was 5–10 kΩ/□, and the carrier mobility was equal to 30–40 cm2/V·s. The most important parameter determining the mobility of carriers in the films obtained from suspensions is found to be the flake thickness. The carrier mobility strongly decreased from ∼100 to 0.05 cm2/V·s when the flake thickness changed from one monolayer to few monolayers (up to ∼ 4–5 nm). This effect is most likely associated with the quality of the connection between the flakes. Only monolayer - bilayer flakes are capable of forming real connections in the film due to van-der-Waals forces.

Язык оригиналаанглийский
Страницы (с-по)1655-1661
Число страниц7
ЖурналCurrent Applied Physics
Том17
Номер выпуска12
DOI
СостояниеОпубликовано - 1 дек. 2017

Fingerprint

Подробные сведения о темах исследования «2D printed graphene conductive layers with high carrier mobility». Вместе они формируют уникальный семантический отпечаток (fingerprint).

Цитировать