Technological characteristics of epoxy/carbon black composites

A. G. Bannov, A. E. Brester, A. A. Shestakov, M. V. Popov, N. I. Lapekin, G. K. Krivyakin

Research output: Contribution to journalConference articlepeer-review

1 Citation (Scopus)

Abstract

The set of epoxy composites based on Alfa AesarTM carbon black (CB) (0-1.5 wt%) has been prepared. Dependence of shaft torque on the rotation frequency in batch mixer with overhead stirrer for epoxy/ CB system was obtained. Chemical resistance tests of epoxy resin/carbon black composites were carried out by sample immersion in 30% H2SO4 and 95% H2SO4. The increase of apparent viscosity of epoxy/CB mixture was observed for relatively low temperatures (30-40 °C). Immersion of epoxy/CB composite in concentrated H2SO4 induced strong oxidation of sample and mass loss. Dilution of sulfuric acid led to the mass gain of the composite sample due to the increased uptake. The improvement of chemical resistance of epoxy/CB composites was observed in 95% H2SO4

Original languageEnglish
Pages (from-to)496-498
Number of pages3
JournalMaterials Today: Proceedings
Volume31
DOIs
Publication statusPublished - 2020
Event6th International Russian-Kazakhstan Conference on Chemical Technologies of Functional Materials, RKFM 2020 - Almaty, Kazakhstan
Duration: 9 Apr 202010 Apr 2020

Keywords

  • Carbon black
  • Chemical resistance
  • Epoxy resin
  • Uptake
  • Viscosity
  • FIBER
  • EPOXY
  • GRAPHITE

Fingerprint

Dive into the research topics of 'Technological characteristics of epoxy/carbon black composites'. Together they form a unique fingerprint.

Cite this