Optical and positron annihilation studies of structural defects in LiInSe2 single crystals

K. Siemek, A. P. Yelisseyev, P. Horodek, S. I. Lobanov, A. A. Goloshumova, A. V. Belushkin, L. I. Isaenko

Research output: Contribution to journalArticlepeer-review

Abstract

Lithium-indium di-selenide (LiInSe2) is a semiconductor material, which has been shown promising for applications in nonlinear optics and neutron detection. LiInSe2 crystals of optical quality, of different (from greenish to red) color were grown. Analysis of the fundamental absorption edge shows allowed direct band-to-band transitions and reveals structural disorder leading to the blurring of the edges of valence and conduction bands. Photoluminescence (PL) intensity is low in LiInSe2 of stoichiometric composition and increases after sample annealing in Se vapors. A narrow line at 408 nm is associated with free excitons. Analysis of PL and PL excitation spectra allows one to associate broad emission bands with point defects as well as with self-trapped excitons. The mean positron lifetime increases after annealing in Se vapor as a result of changes of the dominating defect type. For red crystals only big voids with lifetime of about 1021 ps are observed. Both methods suggest that greenish and red coloring of LiInSe2 are due to Se vacancies and interstitial Se atoms, respectively.

Original languageEnglish
Article number110262
JournalOptical Materials
Volume109
DOIs
Publication statusPublished - 1 Nov 2020

Keywords

  • Absorption
  • Lithium-indium di-selenide
  • Photoluminescence
  • Point defects
  • Positron annihilation
  • Semiconductor

Fingerprint Dive into the research topics of 'Optical and positron annihilation studies of structural defects in LiInSe<sub>2</sub> single crystals'. Together they form a unique fingerprint.