Etching of step-bunched Si(1 1 1) surface by Se molecular beam observed by in situ REM

D. I. Rogilo, L. I. Fedina, S. A. Ponomarev, D. V. Sheglov, A. V. Latyshev

Research output: Contribution to journalArticlepeer-review

3 Citations (Scopus)


Using in situ ultrahigh vacuum reflection electron microscopy, we have first visualized the evolution of step-bunched Si(1 1 1) surface during Se beam etching depending on substrate temperature T and terrace size required for survival of etching-induced vacancies. Below T ~ 630 °C, the etching proceeds in layer-by-layer mode via periodic nucleation of small 2D vacancy islands without noticeable motion of steps. However, in 630–830 °C interval, the etching of the 7 × 7 reconstructed Si(1 1 1) step-bunched surface is realized by both step flow and continuous nucleation and growth of 2D vacancy islands on wide terraces, which leads to the excavation of initially flat surface between step bunches. At T > 830 °C, the etching proceeds by step flow with preservation of initial surface morphology. We have found that the Si(1 1 1) surface etching by Se beam is characterized by 2.65 eV activation energy that limits etching kinetics in low-temperature range when the whole Si(1 1 1) surface is converted to disordered impurity-induced Si(1 1 1)“1 × 1”-Se phase.

Original languageEnglish
Article number125273
JournalJournal of Crystal Growth
Publication statusPublished - 1 Jan 2020


  • A1. Etching
  • A1. Surface processes
  • A1. Surface structure
  • B1. Chalcogenes
  • B2. Semiconducting silicon
  • Chalcogenes
  • Semiconducting silicon
  • Etching
  • Surface processes
  • Surface structure


Dive into the research topics of 'Etching of step-bunched Si(1 1 1) surface by Se molecular beam observed by in situ REM'. Together they form a unique fingerprint.

Cite this